Product Details:
Minimum Order Quantity | 5 PIECE |
Application | N/A |
Width | N/A |
Pack Type | N/A |
Ideal Vehicle Type | N/A |
Thickness | N/A |
Number Of Hole | N/A |
Shape | N/A |
Model | CM 16 |
Brand | Compo |
Additional Information:
Product Details:
Minimum Order Quantity | 50 Meter |
Material | Asbestos |
Thickness (Millimetre) | 4.8 mm to 12.7 mm |
Operating Temperature (Celsius) | 350 |
Transient Temperature (Celsius) | 150 |
Model Number | WA 42 |
Shape | ROLL |
Size (Millimetre) | 15000 mm in Length |
Tensile Strength (kg/Cm Square) | 210 |
Compressive Strength (kg/Cm Square) | 1266 |
Rivet Holding Capacity (kg/CmSq) | 970 |
Brand | COMPO |
Unit pressure | 1-7 kg/cm2 |
Maximum temperature | 350 Deg C |
Maximum continuous temperature | 150 Deg C |
Specific Gravity | 1.65 |
Ultimate tensile strength | 190 kg/cm2 |
Ultimate compressive strength | More than 1600 kg/cm2 |
WA 42
It is a semi- rigid non-metallic, woven asbestos friction material bonded by a high temperature impregnant to give it enhanced mechanical strength and good antifade and wear properties.
The material is sufficiently flexible to accommodate small changes in radius and to make it suitable for use as a band lining. The impregnant does not soften when heated and large changes in radius should not be attempted.
WA-42 is available in liner and roll form and is suitable for use under dry operating conditions (i.e. it is not suitable for use in oil).
APPLICATIONS :-
General purpose automotive drum brakes, Industrial Drum Brakes, Industrial band brakes and clutches (on e.g. excavators, cranes, lifts, electro-magnetic brakes), drive shaft transmission brakes, miscellaneous friction devices.
TECHNICAL DATA :-
Friction m for design purposes : 0.38
PHYSICAL PROPERTIES :-
Data based on standard test method:
Tensile strength : 210 kg/cm2
Ultimate compressive strength : 1266 kg/cm2
Rivet holding Capacity : 970 kg/cm2
Specific gravity : 1.48
Recommended Mating Surface :-
Good quality fine grained or alloy cast iron.If steel, then forged or cold rolled with a brinell hardness of 150 or over. Cast steels are not recommended for use as mating surfaces.
Recommended Operating Temperatures :-
Maximum temperature : 3500C ; Maximum continuous temperature : 1500C
Product Details:
Minimum Order Quantity | 15 Meter |
Specific gravity | 1.9 |
Ult tensile strength | 240 kg/cm2 |
Ult compressive strength | 700 kg/cm2 |
Rivet holding capacity | 1000 kg/cm2 |
Model | WA-10 |
Brand | Compo |
WA10
It is a semi-rigid, solid woven, asbestos-based friction material with a brass wire content. It is primarily intended for use under oil immersed conditions, but can also be used dry.
When in use for an oil-immersed application, should the supply of lubricant fail, WA- 10 will continue to function and avoid immediate failure of the unit. It is available in Roll lining form only.
APPLICATIONS :-
Oil immersed brakes, plate and cone clutches for industrial usage, earth-moving equipment, agricultural machinery etc.,
PHYSICAL PROPERTIES :-
Data based on standard test methods:
Ultimate tensile strength : 240 kg/cm2
Ultimate shear strength : 125 kg/cm2
Ultimate compressive strength : 700 kg/cm2
Rivet holding capacity : 1000 kg/cm2
Specific gravity : 1.9
RECOMMENDED OPERATING RANGE :-
Maximum temperature : 2600C ; Maximum continuous temperature : 1250C
Product Details:
Minimum Order Quantity | 10 Meter |
Hardness | 85 in Rockwell HRL |
Heat Swell | At 200 Deg C 0.15 mm |
Water Swell | 0.02 mm |
Cross Breaking Strength | 400 Kg/cm2 |
Rivet Holding Capacity | 900 per Rivet Hole Diameter (Kg-f) |
Maximum Continuous Operating Temperature | 250 Degree C |
WA - 8
It is a flexible, solid woven, asbestos based friction material made from asbestos yarn, spun around brass wire, which contributes considerably to its strength. WA-8 has a medium/high co-efficient of friction combined with moderate temperature and wear resistance. WA-8 is available in roll form. Segments, Cones and special shapes can easily be cut from it. Being a flexible material, it is possible to form it to radius when fitting it. Forming can be made easier by placing the material in an oven at a temperature of not more than 100°C (212°F) until it has heated throughout to soften the impregnant. WA-8 is designed solely for use under dry conditions (i.e. it is not suitable for use in oil).
WA-8 can also be supplied with both surfaces ground.
APPLICATIONS :-Industrial band and drum brake Linings ;Industrial band, plate and cone clutch linings (eg. cranes, lifts, excavators .winches, concrete mixers, drop hammers, mine widening appliances, underground haulages, tippers, oil well draw works, road rollers, sugar mill centrifuges), certain heavy road transport vehicles and tractors.
TECHNICAL DATA :-Friction µ for design purposes 0.35
PHYSICAL PROPERTIES :-
Data based on standard test methods Specific gravity : 1.6
ult. tensile strength : 246 kg/cm2
ult. compressive strength : 630 kg/cm2
Rivet holding capacity : 900 kg/cm2
RECOMMENDED OPERATING RANGE :-
Maximum continuous temperature : 125o C